Crystallization, formation, and accumulation of defects and mesopores in the ZSM-5 zeolite samples, which are synthesized from the gel composition of 1.2Na2O 0.1Al2O3 0.8 tetra-propylammonium hydroxide (TPAOH) 6SiO2 400H2O at a temperature of 140 degree Celsius (°C) in 10, 15, and 18 h, are studied by using the Positron annihilation lifetime (PALS) and X-ray diffraction (XRD)spectroscopies. The XRD is used for investigating the crystalline concentration and nano-crystal size of ZSM-5 during the crystallizing process, whereas the PALS is performed in order to determine the presence of templates, defects, and mesopores in the zeolite samples. The latter are calcined in air during 1, 2, and 3 h at a temperature of 600 °C before being measured. The results obtained indicate that there exist clusters of small crystals in the early crystalline stages of the samples. The size of these crystals increases with time and reaches approximately 100 nm after 18 h of reaction. In addition, the template (TPAOH) is found to exist not only in the channels inside the framework but also in the mesopores outside it. Finally, by analyzing the Positron lifetime spectra, we have found for the first time the simultaneous existence of defects and mesopores, which are formatted and accumulated during the crystallization of ZSM-5. Those important results contribute significantly to our understanding of the internal structure of the synthetic zeolite ZSM-5 as well as the synthetic processes for producing zeolites with special features.

http://dx.doi.org/10.1063/1.4977013